Although considerable research has been conducted on nitrate reduction by zero-valent iron powder (Fe0), these studies were mostly operated under anaerobic and invariable pH conditions that was unsuitable for practical application.Without reaction conditions (dissolved oxygen or reaction pH) control, this study aimed at subjecting the kinetics of denitrification by microscale Fe0 (160-200 mesh) to analysis the factors affecting the denitrification of nitrate and the composition of iron reductive products coating upon the iron surface.Results of the kinetics study have indicated that a higher initial concentration of nitrate would yield a greater reaction rate constant.Additional test results showed that the reduction rate of nitrate increased with increasing Fe0 dosage.The reaction can be described as a pseudo-first order reaction with respect to nitrate concentration or Fe0 dosage.Experimental results also suggested that nitrate reduction by microscale Fe0 without reaction condition control primarily was an acid-driven surface-mediated process, and the reaction order was 0.65 with respect to hydrogen ion concentration.X-ray diffractometry and X-ray photoelectron spectroscopy indicated that a black coating, consisted of Fe2O3, Fe3O4 and FeO(OH), was formed on the surface of iron grains as an iron corrosion product when the system initial pH was lower than 5.The proportion of FeO(OH) increased as reaction time went on, whereas the proportion of Fe3O4 decreased.