The microstructural features,shape memory behavior and mechanical properties of Ni-Mn based alloys were investigated by dierential scanning calorimetry(DSC),scanning electron microscopy(SEM),transmission electron microscopy(TEM)and thermal cycling test under various stresses.The transformation temperatures shifted toward lower temperatures when adding a third element into the Ni-Mn system.The addition of 10 at. pct Fe increased considerably the mechanical properties exhibiting still high transformation temperatures. However,it was found that in NiMn40Fe10 alloy the martensitic transformation is not thermoelastic in nature. The mechanism of this transformation and the crystallography of Ni-Mn(50-x)-Fex(x=5,7,10,20 at.pct) alloys are presented.
The microstructural features, shape memory behavior and mechanical properties of Ni-Mn based alloys were investigated by dierential scanning calorimetry (DSC), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and thermal cycling test under various various stresses. shifted toward lower temperatures when adding a third element into the Ni-Mn system. The addition of 10 at. However, it was found that in NiMn40Fe10 alloy the martensitic transformation is not thermoelastic in nature. The mechanism of this transformation and the crystallography of Ni-Mn (50-x) -Fex (x = 5,7,10,20 at.pct) alloys are presented.