【摘 要】
：
本发明系含2～4％Si的取向硅钢板的制造方法,其特点在于将成分为2～4％Si、0.04％～0.15％Mn,S(S/Te)=0.1～0.3％Cu和0.035～0.12％Te的钢水连注成坯,并在钢坯冷却到1000℃以前直接进行轧制;如果板
论文部分内容阅读
本发明系含2～4％Si的取向硅钢板的制造方法,其特点在于将成分为2～4％Si、0.04％～0.15％Mn,S(S/Te)=0.1～0.3％Cu和0.035～0.12％Te的钢水连注成坯,并在钢坯冷却到1000℃以前直接进行轧制;如果板坯冷到1000℃以下需要重新加热到1000～1200℃才轧。经冷轧和控制在950℃以下的温度进行中间退火,就可以得到很好的电磁性能。
The present invention relates to a method for producing oriented silicon steel sheet containing 2 to 4% Si. The method is characterized in that the composition is 2 to 4% of Si, 0.04 to 0.15% of Mn, S (S / Te) = 0.1 to 0.3% of Cu and 0.035 ~ 0.12% Te molten steel into a continuous billet, and the billet directly cooled to 1000 ℃ before rolling; if the slab cooled to below 1000 ℃ need to reheat to 1000 ~ 1200 ℃ before rolling. After cold-rolled and controlled at a temperature below 950 ℃ for intermediate annealing, you can get good electromagnetic properties.
其他文献
拖拉机由于工作环境灰尘大,要求易损件有良好的抗磨料磨损的特性,并希望在运转中零件能尽量保持良好的润滑条件,以期达到较长的使用寿命。为了加速实现我国的农业机械化,更
俄产Ｋ－７０２Ｍ装载机轮胎的国产化改造（１５００７０）黑龙江省第四公路工程处李久强王树立张东君唐元军１９９３年我处购进了两台俄罗斯Ｋ－７０２Ｍ装载机。该机液压控制程度高，装载能力强，适用于繁重的土、石方工程。但使
为了满足油泵油嘴、轴承等工业部门对高精度、高光洁度圆柱形零件的磨削要求,我厂职工遵照毛主席“独立自主,自力更生”的教导,在厂党委领导下,组织了“三结合”的研制小组,
在多轴孔加工领域里常常出现一些加工问题,即使采用目前高度发展的多轴钻床仍然解决得很不经济。例如:有些工件一面或多面有大量的孔,常常需要进行顺序加工,即:扩孔、锪平面
在石油化工机械及制氧机设备中,封头这类零件较多,所有容器几乎都采用封头。因此,在制造封头这类零件时,如何正确计算其毛坯直径,对于封头的质量有其重要意义。下面就谈谈如
一、前言 为了迅速赶超世界先进水平,一九七三年三月一机部在广州召开了工具行业会议,总结国内外工具行业发展趋势和特点,提出了要发展钻头自动磨沟、磨尖的新工艺,从而提高
据用户反映,Z47—12型冷镦机在负荷运转中,存在顶料箱联接刚性不足、去料头机构和顶料机构的保险装置工作不可靠等问题。我厂组成以工人为主体的“三结合”小组对上述机构进
这种机构(见图)能够利用半螺母使螺钉大量地移动,并且,也能进行通常的微小移动。在支架1上有一个与螺钉移动方向相同的但是比螺钉直径大的孔2,在其上部有一个和它垂直的铰制
三、双面对接焊缝探伤时各种伪缺陷的判断1.油层反射讯号由于被测面凹凸不平或者是焊缝附近金属飞溅物没有磨平,在探头沿焊缝方向移动过程中,探头楔块与被测面之间局部地方
调整整铁结构的好坏对于长期保持机床精度,避免机床及基础因受力不均而产生变形关系很大,应予足够注意。最近我们在安装进口的大型机床中发现有两种随机带来的调整垫铁,具有