ZnO films with special textures are fabricated on Mo-coated Al 2 O 3 ceramic substrates by the catalyst-free electron beam evaporation method, and the as-deposited films are treated by hydrogen plasma. It is found that the surface morphologies of the films are changed significantly after hydrogen plasma treatment and that the films consist of vertically standing and intersecting nanosheets. A lower turn-on field of 1.2 V/μm and an enhanced current density ～0.11 mA/cm 2 at 2.47 V/μm are achieved. The low threshold field and the high emission current density are attributed primarily to the unique shape and smaller resistivity of the ZnO nanosheet films.
ZnO films with special textures are fabricated on Mo-coated Al 2 O 3 ceramic substrates by the catalyst-free electron beam evaporation method, and the as-deposited films are treated by hydrogen plasma. It is found that the surface morphologies of the films are changed significantly after hydrogen plasma treatment and that the films consist of vertically standing and intersecting nanosheets. A lower turn-on field of 1.2 V / μm and an enhanced current density ~ 0.11 mA / cm 2 at 2.47 V / μm are achieved. The low threshold field and the high emission current density are at primarily to the unique shape and smaller resistivity of the ZnO nanosheet films.