论文部分内容阅读
Continuous-drive rotary friction welding was performed to join cylindrical specimens of carbon steel (EN24) and nickel-based su-peralloy (IN718),and the microstructures of three distinct weld zones—the weld interface (WI)/thermo-mechanically affected zone (TMAZ),the heat-affected zone (HAZ),and the base metal—were examined.The joint was observed to be free of defects but featured uneven flash formation.Electron backscatter diffraction (EBSD) analysis showed substantial changes in high-angle grain boundaries,low-angle grain boundaries,and twin boundaries in the TMAZ and HAZ.Moreover,significant refinement in grain size (2–5 μm) was observed at the WI/TMAZ with reference to the base metal.The possible causes of these are discussed.The microhardness profile across the welded joint shows variation in hardness.The changes in hardness are ascribed to grain refinement,phase transformation,and the dissolution of strengthen-ing precipitates.The tensile test results reveal that a joint efficiency of 100％can be achieved using this method.