Only a few studies have been conducted on the flow behavior of the novel BTW1/Q345R bimetal,which is widely used in coal equipment.In this work,compression tests were conducted on BTW1/Q345R bimetal at a temperature range of 950 ℃-1200 ℃ and strain rates of 0.05,0.5,5,and 15 s1 by using a Gleeble-3800 thermomechanical simulator.A constitutive equation was validated by referring to the Arrhenius equation during the characterization of hot workability.The computed apparent activation energy of the BTW1/Q345R bimetal was 360 kJ/mol,and processing maps under different strain conditions were drawn.Analysis of the stress-strain relationship revealed that work hardening exerted a dominant effect on the thermal deformation of the BTW1/Q345R bimetal.The processing maps predicted that the optimal processing interval will increase with strain.Results showed that thermal deformation of the BTW1/Q345R bimetal should proceed when the temperature range varies from 1182 ℃ to 1200 ℃ and the strain rate interval is from 4.2 to 15 s-1.