A novel type of thermal stabilizer-lanthanum tris (mono- i -octyl phthalate) (LTMP) was synthesized by double-decomposition reaction o f sodium mono- i -octyl phthalate with lanthanum chloride at 60 ℃. Sodium m ono- i -octyl phthalate was prepared by sodium hydrate and mono- i -octy l phthalate prepared by reaction of isooctyl alcohol and phthalic anhydride in th e presence of sulfuric acid catalyst at 110 ℃. The yield of lanthanum tris (mon o- i -octyl phthalate) is about 84.5%. Its thermal stabilities were measured by heat-ageing oven test when incorporated into PVC. The experimental results show that the heat stability time is about 40min at 190 ℃ when adding 3phr (pe r hundred resin) to PVC. The thermal stability of this product is better than th at of Ca-Zn complex and basic lead salt stabilizers, and equal to that of dibut yltin dilaurate.
A novel type of thermal stabilizer-lanthanum tris (mono-i -octyl phthalate) (LTMP) was synthesized by double-decomposition reaction of sodium mono-i -octyl phthalate with lanthanum chloride at 60 ° C. Sodium m ono- i -octyl phthalate was prepared by sodium hydrate and mono- i -octy l phthalate prepared by reaction of isooctyl alcohol and phthalic anhydride in th e presence of sulfuric acid catalyst at 110 ° C. The yield of lanthanum tris (mon o-i -octyl phthalate) is about 84.5%. Its thermal staging were incorporated into PVC. The experimental results show that the heat stability time is about 40min at 190 ° C when adding 3phr (pe r hundred resin) to PVC. The thermal stability of this product is better than th at of Ca-Zn complex and basic lead salt stabilizers, and equal to that of dibut yltin dilaurate.