采用半固态成形技术(SSM)代替传统铸造来生产汽车用盒形件。基于Power Law Cut-Off(PLCO)模型和有限元模拟软件ProCast2008对盒形件半固态压铸过程建立模型并进行数值模拟,揭
【机 构】
：
西安交通大学机械工程学院,黎贵敦理工大学,
论文部分内容阅读
采用半固态成形技术(SSM)代替传统铸造来生产汽车用盒形件。基于Power Law Cut-Off(PLCO)模型和有限元模拟软件ProCast2008对盒形件半固态压铸过程建立模型并进行数值模拟,揭示了主要工艺参数对成形过程的影响规律。结果表明,在盒形件半固态压铸过程中,浇注温度、冲头速度、模具加热温度有明显的影响,并进一步获得了半固态压铸的合理工艺参数。
Semi-solid forming technology (SSM) instead of the traditional casting to produce automotive boxes. Based on the model of Power Law Cut-Off (PLCO) and finite element simulation software ProCast2008, the model of semi-solid die-casting process was established and numerical simulation was carried out. The influence of main process parameters on the forming process was revealed. The results show that the pouring temperature, the punch speed and the heating temperature of the mold have a significant influence on the semi-solid die-casting of the box-shaped parts, and the reasonable process parameters of semi-solid die-casting are obtained.
其他文献
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
研究了铜铝复合带退火工艺对同轴电缆用铜铝复合带组织和性能的影响。结果表明,铜铝复合带合理的退火工艺为310℃×1h,此时复合带的抗拉强度为78MPa,伸长率为23.17%,杯突
采用金相显微镜、SEM及EDS等分析手段对Cu/Al冷轧复合界面结合机理进行研究,建立扩散退火阶段不同轧制压下率时的扩散层生长动力学方程,并探讨了不同压下率对界面扩散层生长
使用65％杀·苄可湿性粉剂375 g,750 g和1125 g/hm~2防治水稻1代二化螟和本田期杂草,表现出良好的兼防作用,对枯心的防效分别为91.99％,96.36％和100.00％,对本田期杂草的防效分别为7
利用铸渗法制备了WC颗粒增强钢基表面复合材料,通过金相、扫描电镜等测试手段,重点研究了预制层中添加Ni粉对WC/钢基表面复合材料组织和界面的影响。结果表明,随着Ni添加量的
经930℃和1 030℃过热处理后,采用水淬法制备了直径为5 mm的Cu400Zr45Al7Ag8大块非晶合金.利用差示扫描量热仪(DSC)对其晶化行为进行了研究.并通过X射线衍射分析了Cu400Zr45A
国外玉米种质的引进、利用与改良是我国玉米杂交育种不可缺少的重要环节,也是育种成败的关键。选用从欧洲引进的21个玉米杂交种,在经过产量比较鉴定和农艺性状综合评判后,选
对比了Al-5Ti-0.4C、Al-5Ti-1B及Al-3Ti-1B-0.2C中间合金对A356合金的晶粒细化行为。发现在730℃时,加入0.2%的Al-3Ti-1B-0.2C中间合金,可以使A356合金的晶粒尺寸由1000μm以
针对高铝青铜粉体材料的涂覆应用,采用HVOF技术制备铝青铜(Cu-14Al-X)粉体材料涂层,并与304不锈钢进行滑动干摩擦试验,结合扫描电子显微镜、能谱和电子探针等手段研究涂层的
采用透射电镜(TEM)、X射线衍射(XRD)和压缩试验,研究了氩气压力和稀释剂对铝热法制备的块体纳米晶Fe3Al材料组织和性能的影响。结果表明,在氩气压力分别为3、6、9MPa和稀释剂