The structural and phase transformations occurring in the near-surface layers of pre-quenched W6Mo5Cr4V2high-speed steel (HSS) subjected to intensity pulsed ion beam (IPIB) melting have been investigated. The effect of IPIB high beam current density of 80A/cm2, acceleration voltage of 250kV, pulse duration of 70 ns. Samples were bombarded with 1, 3, 5 pulses respectively. It has been revealed that after IPIB irradiation the initial martensite in the near-surface layer of HSS changed into austenite and produced residual stresses by using electron microscopy and X-ray diffraction.Redistribution and interlace of dislocations in the irradiated samples were generated under the impact of shock wave. With increasing pulse times gradual liquid-phase dissolution of M6C carbide particles occurs in the near-surface layer and produces nanocrystalline MC. This process results in the decrease of martensite crystal (α-phase) and increase of austenite (γ-phase) content and the dispersed carbide. Wear resistance of the HSS is improved by a factor of 2, which is explained by the formation of metastable phases such nanocrystal and residual stresses and the redistribution and interlace of dislocations.