In this paper, surface photovoltage spectroscopy (SPS) is used to determine the electronic structure of the hydro-genated transition Si films. All samples are prepared by using helicon wave plasma-enhanced chemical vapour deposition technique, the films exhibit a transition from the amorphous phase to the microcrystalline phase with increasing temperature. The film deposited at lower substrate temperature has the amorphous-like electronic structure with two types of dominant defect states corresponding to the occupied Si dangling bond states (D0/D-) and the empty Si dangling states (D+). At higher substrate temperature, the crystallinity of the deposited films increases, while their band gap energy decreases. Meanwhile, two types of additional defect states is incorporate into the films as compared with the amorphous counterpart, which is attributed to the interface defect states between the microcrystalline Si grains and the amorphous matrix. The relative SPS intensity of these two kinds of defect states in samples deposited above 300 C increases first and decreases afterwards, which may be interpreted as a result of the competition between hydrogen release and crystalline grain size increment with increasing substrate temperature.