【摘 要】
：
列出了6Cr4Mo3Ni2WV基体钢的机械性能与回火温度的关系。用电镜薄膜技术等研究了组织结构,着重观察了硬度—回火温度曲线峰值附近的结构。指出合金的二次硬化主要由V_4C_3和
论文部分内容阅读
列出了6Cr4Mo3Ni2WV基体钢的机械性能与回火温度的关系。用电镜薄膜技术等研究了组织结构,着重观察了硬度—回火温度曲线峰值附近的结构。指出合金的二次硬化主要由V_4C_3和M_2C析出产生。回火时沿马氏体内挛晶界和{112}晶面析出的片状渗碳体,低于450
The relationship between the mechanical properties of 6Cr4Mo3Ni2WV matrix steel and tempering temperature is listed. The structure of the microstructure was studied by using the electron microscopy and other techniques. The structure around the peak of the hardness-tempering temperature curve was observed. It is pointed out that the secondary hardening of the alloy is mainly caused by the precipitation of V_4C_3 and M_2C. Tempering along the martensite within the crystal boundaries and {112} crystal surface of the plate-like cementite precipitation, less than 450
其他文献
显示良好耐蚀性能的奥氐体不锈钢在比较缓和的腐蚀环境中竟有局部腐蚀的致命弱点,外部应力腐蚀破裂(以下称ESCC,亦即:Externat Stress Corrosian Cracking),就是其典型例子。
加纳在1983年实行经济改革以来,几个重要的经济指标都引人注目地上升了。国内生产总值连续三年增长5％以上,作为加纳经济支柱的可可产量这两年提高了28％,出口收入在三年中增长4
工业生产要求铸铁件材质进一步提高,例如,要求孕育铸铁高强度、同时具有高致密性;要求球墨铸铁在铸态具有良好综合机械性能并具有低温抗冲击韧性。 如何高效孕育处理以改善
长期以来,航空辅机工厂的各种冷冲压模具多半都是采用精度较高的导柱和导套作导向机构的,没有充分利用冲床滑块的导向精度,这对于精度要求高的军品来说是完全必要的。但目前
本文根据焊条自动焊的特点,提出了一种具有电弧电压闭环负反馈的焊条自动施焊控制系统,并给出了系统相应的框图。文中还通过详细的理论分析与计算,证明一般焊条自动焊机在无
本文介绍了光滑极限量规的计算机辅助设计(CAD),用 BASIC 语言编制了设计量规的计算及绘图程序,井已复制在51/4英寸软盘上,只要输入已知的设计参数,便能自动地显示(或打印)出
本文对于用磁化处理的高速钢刀具车削中碳钢时,在一定条件下能够显著提高刀具耐用度的现象进行了分析,得出了某些内在规律。通过二次正交组合设计,研究了切削速度、进给量、
合肥矿山机器厂铸造车间有一台10m~2台车式铸件热处理炉,工作温度950℃,最大装炉量25t,台车尺寸为4000×2500mm,采用滚柱传动。台车牵引原采用水平轴内滑轮行车牵引结构,利
一、前言超高压模具广泛应用于金属液静挤压、冷挤压及人造金刚石等工艺。由于内压一般均在10000bar以上,往往超过了单层常用金属材料的承载能力,必需采用预应力组合式模具
本文介绍了磁化电解渗硫工艺和渗硫层的组织、性能,并对服役不同时间的磁化渗硫零件的表面形貌等进行了观察和分析,同时还探讨了磁场的作用。作者认为,磁化电解渗硫是很有发