【摘 要】
：
The existence of yttrium in Ti-23Al-25Nb alloy and its influence on the microstructure after heat treatment of Ti-23Al-25Nb alloy were investigated using therma
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
The existence of yttrium in Ti-23Al-25Nb alloy and its influence on the microstructure after heat treatment of Ti-23Al-25Nb alloy were investigated using thermal analysis(DTA),EPMA,XRD and SEM. The heat treatment was determined based on DTA measurements. The compression tests at room temperature were performed on a Instron-569 universal tester. The results show that yttrium exists as the Y2O3 alloy. The addition of Y doesnt affect the characteristic phase transformation temperature. At lower quenching temperature,Y strengthens the XRD peaks of O phase by improving the decomposition of B2 phase. Yttrium addition enhances the compression properties with the compression strength,yield strength and compression ratio increasing. The strengthening is attributed to the second phase strengthening of Y2O3 particles and the grain refinement.
其他文献
This is a synthetical report about hydrogen behavior in titanium aluminide alloys in our group. There are two kinds of hydrogen solubility in titanium aluminide
The catalytic performance of perovskite composite oxide catalyst La0.9 K0.1 CoO3 coated on catalyst supports by trnditional solid state reaction method and sol-
The evolution of ordered interphase boundary (IPB) of Ni75AlxV25-x alloys was simulated using the microscopic phase-field method. Based on the atomic occupation
Materials with negative thermal expansion have many important applications such as constituents of composite materials designed to .reduce their overall thermal
The axial mixing is a key factor for design and scaling up of the pulsed extraction column which has strong influence on the mass transfer performances of the p
One way of improving the magnetic properties of RECo5 (RE=rare earth) compounds, especially the magnetic anisotropy energy (MAE), is to dope them with some addi
The optical properties of blue emitting BaAl2S4:Eu thin-films were studied. The emission peak is around 470 nm, whose FWHM (full width at half maximum) is 35 nm
Transparent polycrystalline yttria is a promising optical ceramics with excellent physical and chemical properties. A commercial yttria powder with a mean parti
The formation ability and thermal stability of phosphate laser protection glass doped with high Sm2O3 content were discussed. The characteristic temperatures (T
316L stainless steel samples,as a widespread used material,were irradiated with HIPIB at the beam parameters of ion energy 300 keV,current density 100,200 and 3