剧烈塑性变形对AZ31镁合金显微组织和力学性能的影响

来源 :2012 Postdoctoral Symposium of China on Materials Science & | 被引量 : 0次 | 上传用户：monzad

【摘要】

：

通过等通道转角挤压技术(ECAP)对镁合金进行剧烈塑性变形，使用有限元法实现对ECAP加工过程及相关工艺参数的数值模拟，分析成形过程中的网格的变化、应力应变分布规律及其加载载荷规律，确定主要工艺参数影响规律。通过分析，得出晶粒细化程度与力学性能的关系，为镁合金的晶粒细化方法提供更合理的理论指导和参考依据。

【出处】

：

2012 Postdoctoral Symposium of China on Materials Science &

【发表日期】

：

2012年8期

【关键词】

：

镁合金 AZ31合金等通道转角挤压工艺参数晶粒细化

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

Preparation and dielectric properties Barium strontium titanate niobate composite ceramics by powder

Barium strontium titanate niobate (BST/SBN) composite ceramics system following the general formula 0.7BaO·0.3SrO·(1-y)TiO2·yNb2O5 were firstly prepared by the modified Powder-Sol method.By controllin

会议

Powder-soldielectric propertiesperovskite phasetungsten bronze phase

Topology optimization of microstructure and selective laser melting fabrication for metallic biomate

The precise design and fabrication of biomaterial scaffolds is necessary to provide a systematic study for bone tissue engineering.Biomaterial scaffolds should have sufficient stiffness and large poro

会议

Topology optimizationselective laser melting (SLM)microstructuremetallic biom

Microstructure and corrosion behavior of micro-arc oxidation film on magnesium alloy

The microstructure, composition and elemental depth profile of micro-arc oxidation film was analyzed by means of Scanning Electron Microscope (SEM), X-ray diffraction (XRD) and Energy Disperse Spectro

会议

Magnesium alloymicro-arc oxidationstructurecorrosionEIS

Effect of annealing temperature on the microstructural and optical-electrical properties of Cu-Al-O

We have successfully prepared Cu-Al-O thin films on silicon (100) and quartz substrates by RF magnetron sputtering method.The as-deposited Cu-Al-O film is amorphous in nature and post-annealing treatm

会议

Cu-Al-O filmannealingelectrical resistivityoptical band gap

Research on glass material's micro milling brittle-ductile transition mechanism

Glass material has many fine chemical properties and is widely used in hi-tech fields such as aerospace and biomedical.But its also a typical hard processing material since its brittle and very hard.M

会议

Optical glassmicro milling machiningsurface roughnessbrittle ductile transiti

The microstructures and formation mechanism of headstand pyrocarbon cones developed by electromagnet

A novel headstand pyrocarbon cones (HPCs) with hollow structure was developed at 650-750 ℃ by the electromagnetic-field-assisted chemical vapor deposition.It is observed that the HPCs can form on the

会议

Headstand pyrocarbon coneschemical vapor depositionelectromagnetic-field-assis

模具参数对楔横轧铝合金轧件内部空洞的影响

通过分析楔横轧内部空洞(疏松)缺陷的物理性质和形成特征，将内部空洞视为多孔材料，利用多孔材料的刚塑性有限元方法，建立7075铝合金坯料内部空洞缺陷的数值模型。采用相对密度研究成形角、展宽角、断面收缩率对内部空洞缺陷的影响规律。结果显示：内部空洞的扩展主要发生在展宽段，楔入段对它的影响很小。展宽角是影响内部空洞产生的主要因素，而断面收缩率的影响较小。成形角、展宽角、断面收缩率越大，越不易发生内部空洞

会议

7075铝合金多孔材料楔横轧内部空洞相对密度

时效温度与时间对6005A铝合金挤压型材显微组织与力学性能的影响

研究时效时间和时效温度对6005A铝合金显微组织与力学性能的影响,对该铝合金挤压型材进行人工时效实验,时效时间分别为4、8和12h,时效温度分别为150、175和200℃.结果表明：随着时效温度和时间增加,挤压过程形成的粗大Al(Fe,Cr)Si析出相形貌由颗粒状向棒状转变,175℃时亚微米级析出相体积分数最大,200℃时在晶界析出1～3μm左右的AlFeSi相.挤压型材的室温力学性能对时效工艺中

会议

6005A铝合金挤压时效Al(FeCr)Si颗粒AlFeSi颗粒显微组织力学性能

双曲率飞机整体壁板压弯成形有限元建模

为了建立压弯成形工艺的有限元模型，提出一种特殊的模拟过程和一种基于压弯线坐标的上下模边界条件计算方法。实现了双曲率飞机整体壁板七道次压弯成形工艺的模拟并且可以较好地模拟真实的生产过程，本建模方法可用于此复杂成形工艺的研究。分析了应力和应变分布，揭示了成形工艺的变形机理。通过进行定量的比较，得知七道次压弯成形的成形精度和表面质量较好。

会议

压弯成形飞机整体壁板双曲率外形有限元建模

基于数值模拟的金属板材渐进成形板厚分布与力学性能分析

以方锥台为基准模型，采用数值模拟和拉伸试验研究金属板材渐进成形的板材厚度分布与力学性能，建立渐进成形有限元模型并进行试验验证，通过对成形工具头的位移约束来保证有限元模型中的成形轨迹与实际加工时一致。验证正弦法则预测板厚的有效性，研究成形轨迹与最小板厚及其位置的关系。结果表明：该法则只适用于以纯拉伸变形方式为主的成形区域，最小板厚与工具头直径密切相关，而其位置则决定于层间距，成形后的零件拉伸试验表明

会议

渐进成形数值模拟板厚塑性强度

剧烈塑性变形对AZ31镁合金显微组织和力学性能的影响

其他学术论文