【摘 要】
：
Deformation of bulk amorphous Al2O3-ZrO2 with different ratios of A/Z was investigated under compression at 500℃.A20Z and A40Z exhibited brittle fracture and remained amorphous after compression;howev
【机 构】
：
Key Laboratory for Advanced Ceramics and Machining Technology of Ministry of Education,School of Mat
论文部分内容阅读
Deformation of bulk amorphous Al2O3-ZrO2 with different ratios of A/Z was investigated under compression at 500℃.A20Z and A40Z exhibited brittle fracture and remained amorphous after compression;however,significant plastic deformation was achieved in A60Z and A80Z.Nanocrystallite of t-ZrO2 were detected in A60Z and A80Z during the plastic deformation,and deformation-induced nanocrystallization in amorphous oxides was reported for the first time.Ductile transformation temperature was proposed as a criterion for the deformability of amorphous materials.The nanocrystallization improved the plasticity in turn,due to the easier formation of multiple shear bands at the interface between nanocrystallite and amorphous matrix.Crystallization activation energy was identified as a key factor dominating the deformation of amorphous oxides,and low crystallization activation energy could contribute to easy nanocrystallization,lower the ductile transformation temperature,and promote the plasticity.This work gave further understanding of plastic deformation in amorphous oxides.
其他文献
Directional ice-templated ceramics have unique lamellar porous channels between ceramic walls which run from bottom to top of the samples.This highly oriented morphology results in the anisotropy in m
印尼海德堡P14项目烧成系统采用了国产化的万吨级预分解系统和万吨级回转窑.针对印尼当地高水分原料和高水分褐煤的特点,对预热器、分解炉、回转窑等设备进行了优化设计.实际运行结果反馈,烧成系统能耗指标和环保指标均达到同规模生产线的先进水平,顺利通过性能考核.
Silica sol is one of the frequently-used binders in high-temperature resistingfibrous porous ceramics,but in the drying process,it can diffuse with water and influencethe uniformity of ceramics.To sol
The influences of different fibers and F ions on the formation mechanism of hierarchical structure were investigated.This study was undertaken to better understand how fibers affect the growth of mull
A room temperature curable heat-resistant adhesive with broad working temperature rangewas prepared through organic and inorganic modification.The preceramic polymethylsiloxane showedlow bonding stren
MoSi2-borosilicate glass coating with MoSi2 as emittance agent was prepared on mullite fibrous ceramics for enhanced superficial infrared radiation via an in-situ reaction method.The phase and structu
Two infrared radiating coatings with borosilicate glass as binder and MoSi2 as emittance agent were prepared on mullite fibrous ceramics by an in-situ reaction method and a two-step method,respectivel
高强度熟料是每个水泥生产企业的内在需求.但与之匹配的高率值生料,易烧性过差,影响工艺操作,难以稳定煅烧连续生产.合理使用矿化剂改善易烧性,减轻窑烧成负荷可为预分解窑系统生产高强度熟料开辟新途径.本文研究了适合预分解窑系统的矿化剂,原料全部来自工业废渣和尾矿.建立了以易烧性系数和矿化系数双参数的等级划分,并以此评价矿化剂效果.采用正交试验法对矿化剂因素水平进行了研究,找到了复合矿化剂的最优组合.即带
The self-healing behavior of MoSi2/borosilicate glass composite was investigated by comparing the flexure strength of pre-scratched specimens before and after healingtreatment.The post-healing strengt
研发了以六级预热器、低氮分解炉、两档短窑、中置辊破冷却机为典型代表的烧成技术,集成应用在水泥窑烧成系统上,达到了低能耗的技术指标,可比熟料热耗≤640kcal/kg.cl,可比标煤耗≤91.4kgce/t.cl,自脱硝效率≥50％,与能耗限额标准新建企业的准入值相比节煤率10％以上,在河南孟电、印尼BOSWA、沙特UCIC等多个项目中成功应用,节能减排效果显著,实现了有竞争力的先进烧成技术推广应用