In this study,recovery processes of isotactic polypropylene(iPP)melted spherulites at 135 ℃ after melting at higher temperatures(170–176 ℃)were investigated with polarized optical microscopy and Fourier transform infrared spectroscopy.The recovery temperature was fixed to exclude the interference from heterogeneously nuclei.After melting at temperatures between 170 and 174 ℃,the melted spherulite could recover back to origin spherulite at the low temperature.Interestingly,a distinct infrared spectrum from those of iPP melt and crystal was observed in the early stage of recovery process after melting at low temperatures,where only IR bands resulting from short helices with 12 monomers or less can be seen,which indicates that the presence of crystal residues is not the necessary condition for the polymer memory effect.Avrami analysis further indicated that crystallization mainly took place in melted lamellae.After melting at higher temperatures,melted spherulite cannot recover.Based on above findings,we proposed that the memory effect can be mainly ascribed to melted lamellae,during which crystalline order is lost but conformational order still exists.These conformational ordered segments formed aggregates,which can play as nucleation precursors at low temperatures.